一、產(chǎn)品性能指標(biāo):

性能 Properey GGD-1 GGD-2 GGD-3 GGD-4 GGD-5
牌號(hào) Brand
化學(xué)成分(%)Chemical composition SiO2≥ 95 96 96 97 90
  Al2O3≤ 0.7 0.6 0.6 0.5 0.4
  Fe2O3≤ 0.5 0.5 0.4 0.4 0.8
冷態(tài)耐壓強(qiáng)度(Mpa)
Cold crushing strength
1350℃×3h
After firing at
15 15 10 10 25
顯氣孔率(%)
Apparent porosity 
1350℃×3h
After firing at
26 26 25 25 23
燒后線變化率(%)Linear changing after burnt 1350℃×3h
After firing at
0~+1.6 0~+1.6 0~+1.2 0~+1.2 0~+1.0
體積密度(g/cm3)Bulk density  1350℃×3h
After firing at
2.0 2.0 2.1 2.1 2.2
耐火度(℃)
Refractoriness
1630 1650 1650 1680
集料粒度(mm)Max. 
grain size of aggregate
5 4.5 4.5 4.2 4.2
施工用量(kg/m3)
Amount for construction
2300 2300 2300 2400 2400
施工方式
Mathod of construction
振動(dòng)或搗打 Jolt or ramming
應(yīng)用  
Application
  青銅bronze 紫銅.黃銅copper  brass 白銅cupronickel   鋼.鐵stee l    鋁及合金aluminium 
  金屬熔煉爐、保溫爐 
Melting furance for nonferrous metals
特點(diǎn)
Characteristic
價(jià)廉  保溫  節(jié)電  不沾渣  快速干燥  化學(xué)結(jié)合  耐侵蝕Cost down Thernalinsulation Economy 
electricity Nostickresidue Fast drying Chemicalbonded Corrosion r

 

?